Zanglamas po'latdan yasalgan 420 / 420J1 / 420J2 lasan
| Texnik xususiyatlari | ASTM A240, ASME SA240 |
| Standart | JIS, ASTM, AISI, GB, EN, DIN |
| Yuzaki | 2B, BA, HL, № 4, Mirror va boshqalar. |
| Tugatish | Sovuq haddelenmiş, Issiq haddelenmiş |
| Qalinligi | 0,3 mm ~ 200 mm |
| Hajmi | 0,3 mm ~ 200 mm |
| Uzunlik | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm va boshqalar |
| Kengligi | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm va boshqalar |
Zanglamas po'latdan yasalgan 420 / 420J1 / 420J2 rulonlari uchun sinf xususiyatlari
| STANDART | WERKSTOFF NR. | UNS | EN | BS | AFNOR | SIS | JIS | AISI |
| SS 420 | 1.4021 | S42010 | X20Cr13 | 420S29 / 420S37 | - | 2303 | SUS420J1 | 420 |
| SS 420J1 | 1.4021 | S42010 | X20Cr13 | 420S29 | Z20C13 | 2303 | SUS420J1 | 420L |
| SS 420J2 | 1.4028 | S42000 | X20Cr13 | 420S37 | Z20C13 | 2304 | SUS420J2 | 420M |
SS 420 / 420J1 / 420J2 sariqlarining kimyoviy xususiyatlari
| Sinf | C | Si | Mn | P | S | Kr |
| SS 420 | 0,16 - 0,25 | maksimal 1 | maksimal 1,5 | maksimal 0,04 | maksimal 0,015 | 12 - 14 |
SS 420 / 420J1 / 420J2 sariqlarining mexanik xususiyatlari
| Rm - tortishish kuchi (MPa) (+ QT) | 650-950 |
| Rp0.2 0,2% chidamlilik kuchi (MPa) (+ QT) | 450-600 |
| KV - zarba energiyasi (J) bo'ylama., (+ QT) | + 20 ° 20-25 |
| A - min. sinish paytida cho'zish (%) (+ QT) | 10-12 |
| Vikersning qattiqligi (HV): (+ A) | 190 - 240 |
| Vikersning qattiqligi (HV): (+ QT) | 480 - 520 |
| Brinellning qattiqligi (HB): (+ A)) | 230 |