Qotishma 30CrMo po'latdan yasalgan lasan
30CrMo po'latdir muhandislik va mashinasozlik konstruktsiyasi uchun Xitoyning qotishma po'latdir, yuqori quvvat va yuqori chidamlilikka ega va 500 ° C dan past haroratlarda yuqori haroratga chidamliligiga ega. 30CrMo materiali yaxshi ishlov berish qobiliyatiga, o'rtacha sovuq bükme va plastisiteye, yuqori sertleşebilirliğe, yaxshi payvandlanishga ega va odatda sozlangan holatda ishlatiladi.
O'lchamlarni etkazib berish doirasi
Qalinligi | 0,1 --- 20 mm |
Kengligi | 1000-3000mm (odatda 1000-2200mm ishlatiladi) |
Uzunlik | 1000-12000 mm yoki sizning so'rovingiz bo'yicha |
Kimyoviy tarkibi (massa%)
C (%) | Si (%) | Mn (%) | Cr (%) | Mo (%) |
---|---|---|---|---|
0.26-0.34 | 0.17-0.37 | 0.40-0.70 | 0.80-1.10 | 0.15-0.25 |
Mexanik xususiyatlar
Rp0.2 (MPa) | Rm (MPa) | Ta'sir KV (J) | Uzayish A (%) | AZ (%) | Yetkazib berish | Qattiqlik HB |
---|---|---|---|---|---|---|
737 (≥) | 647 (≥) | 33 | 41 | 13 | Qaror va qarish, Ann, Ausaging, Q + T | 142 |
30CrMo qotishma po'latdan foydalanish
30CrMo qotishma po'latdan ish harorati 400 ° C dan past bo'lgan po'lat quvurlarni, ishchi harorati 450 ° C dan past bo'lgan mahkamlagichlarni qozonlarda va bug 'turbinalarida, ish harorati 500 ° C dan past va yuqori bosimli yong'oq va gardishlarda va umuman yuk ishlab chiqarishda foydalanish mumkin. texnika; 250 ° C dan past bo'lgan azot-vodorodli vallar, viteslar, boltlar, tirgaklar, manipulyatorlar, yuqori bosimli o'tkazgichlar va payvandlash vositalari.
Ekvivalent
AQShning ASTM, Evropa Ittifoqi (Germaniya DIN EN, Britaniyaning BS EN, Frantsiya NF EN ...), Yaponiyaning JIS va ISO standartlariga teng bo'lgan 30CrMo po'latdir. (Malumot uchun)
30CrMo material ekvivalenti | |||||||||||||
Xitoy | AQSH | Yevropa Ittifoqi | Yaponiya | ISO | |||||||||
Standart | Sinf | Standart | Sinf | Standart | Sinf (Chelik raqami) | Standart | Sinf | Standart | Sinf | ||||
GB / T 3077 | 30CrMo | AISI, SAE ASTM A29 / A29M | AISI 4130 | DIN EN 10083-3 | 25CrMo4 (1.7218), 34CrMo4 (1.7220) | JIS G 4053 | SCM430 | ISO 683-1 | 25CrMo4 |
Standart | Sinf | C | Si | Mn | P | S | Kr | Mo |
EN10083 | 25CrMo4 | 0.22-0.29 | -0.4 | 0.6-0.9 | .00.025 | -0.035 | 0.9-1.2 | 0.15-0.3 |
1.7218 | ||||||||
ASTM A29 | 4130 | 0.28-0.33 | 0.15-0.35 | 0.4-0.6 | -0.035 | -0.04 | 0.8-1.1 | 0.15-0.25 |
JIS G4105 | SCM430 | 0.28-0.33 | 0.15-0.35 | 0.6-0.85 | -0.035 | -0.04 | 0.9-1.2 | 0.15-0.3 |
GB 3077 | 30CrMo | 0.26-0.34 | 0.17-0.37 | 0.4-0.7 | -0.035 | -0.035 | 0.8-1.1 | 0.15-0.25 |
Biz ko'proq ta'minlay olamiz.
15Cr 17Cr3; 20Cr 20Cr4; 30Cr 34Cr4; 40Cr 41Cr4; 45Cr 41Cr4;
30CrMo 25CrMo4; 35CrMo 34CrMo4; 42CrMo 42CrMo4;
38CrMoAL 41CrAlMo7; 50CrVA 51CrV4; 40CrMnMo 42CrMo4;
12CrMo 13CrMo44 (1.7335); 15CrMo 16CrMo44 (1.7337);
20CrMo 25CrMo4 (1.7218); 30CrMo 34CrMo4 (1.7220);
35CrMo 34CrMo4 (1.7220); 42CrMo 42CrMo4 (1.7225);
38CrMoAl 34CrAlMo5 (1.8507); 15CrMnMo 15CrMo5 (1.7262);
20CrMnMo 20CrMo5 (1.7264); 35Cr 34Cr 4 (1.7033);
40Cr 41Cr4 (1.7034); 30Mn2 28Mn6 (1.5065);
35Mn2 36Mn5 (1.5067)
65Mn, SAE1566,55SiMnVB, 60Si2Mn, SAE9260, SUP6 / SUP7,61SiCr7, 60C2,60CrMnBA, 51B60H, SUP11A, 20Cr, SAE2150, SCr420, 17Cr3,40Cr, SAE5140, SCr4
60CrMnA, SAE5160, SUP9A, 60Cr3,40Mn2, SAE1340, SMn438,38MnB5, 42MnL 40CrL