316 / 316L zanglamas po'latdan yasalgan lasan
| Texnik xususiyatlari | ASTM A240, ASME SA240 |
| Standart | JIS, ASTM, AISI, GB, EN, DIN |
| Yuzaki | 2B, BA, HL, № 4, Mirror va boshqalar. |
| Tugatish | Sovuq haddelenmiş, Issiq haddelenmiş |
| Qalinligi | 0,3 mm dan 100 mm gacha |
| Hajmi | 1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm |
Zanglamas po'latdan yasalgan 316 / 316L rulonlari uchun sinf xususiyatlari
| STANDART | WERKSTOF Yo'q | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
SS 316 / 316L sariqlarining kimyoviy xususiyatlari
| Sinf | C | Mn | Si | P | S | Kr | Mo | Ni | Fe |
| SS 316 | Maksimal 0,08 | Maksimal 2.0 | 1,0 max | Maksimal 0,045 | Maksimal 0,030 | 16.00 - 18.00 | 2.00 - 3.00 | 11.00 - 14.00 | 67.845 min |
| SS 316L | Maksimal 0,035 | Maksimal 2.0 | 1,0 max | Maksimal 0,045 | Maksimal 0,030 | 16.00 - 18.00 | 2.00 - 3.00 | 10.00 - 14.00 | 68.89 min |
SS 316 / 316L sariqlarining mexanik xususiyatlari
| Zichlik | Erish nuqtasi | Mustahkamlik chegarasi | Hosildorlik kuchi (0,2% ofset) | Uzayish |
| 8,0 g / sm3 | 1400 ° C (2550 ° F) | PSI - 75000, MPa - 515 | PSI - 30000, MPa - 205 | 35 % |
| 8,0 g / sm3 | 1399 ° C (2550 ° F) | PSI - 75000, MPa - 515 | PSI - 30000, MPa - 205 | 35 % |