Zanglamaydigan po'latdan olti burchakli quvurlar va quvurlar
Ta'minot doirasi
| Hajmi | 13-85 mm |
| WT | 0,5-1,8 mm |
| Standart | ASTM A249, A269, A312, A358, A409, A554, A778, A789, A790 |
| Sinflar | 201/202/301/304 / 304L / 316 / 316L / 310S / 409L / 430/416 / va boshqalar |
| Uzunlik | 13mm - 85mm yoki so'ralganda |
| Yuzaki ishlov berish | №1 - 2B - Mat rang - # 400 Yorqin - # 600 Yorqin - 6K Oyna - 8K Oyna - Soch chizig'i |
| Yetkazib berish sharti | Yorqin tavlangan, sayqallangan yoki tavlangan va tuzlangan |
| Hajmi (a × b) | Qalinligi |
| 13,8 × 15,9 | 1.0-1.8 |
| 16 × 18 | 1.0-1.8 |
| 17 × 19 | 1.0-1.8 |
| 19 × 22 | 1.0-1.8 |
| 22 × 25 | 1.0-1.8 |
| 31 × 32 | 1.0-1.8 |
| 33 × 38 | 1.0-1.8 |
| 49 × 50 | 1.0-1.8 |
| 55 × 62 | 1.0-1.8 |
| 55 × 63 | 1.0-1.8 |
| 67 × 76 | 1.0-1.8 |
Kimyoviy tarkibi
| Tarkibi,% | ||||||||
| Sinflar | C | Mn | P | Si | S | Kr | Ni | Fe |
| 304 | Maksimal 0,08 | 2.00 max | Maksimal 0,045 | Maksimal 1,00 | Maksimal 0,03 | 18.0-20.0 | 8.0-10.5 | Balans |
| 304L | Maksimal 0,03 | 2.00 max | Maksimal 0,045 | Maksimal 1,00 | Maksimal 0,03 | 18.0-20.0 | 8.0-12.0 | Balans |
| 304H | 0.04-0.10 | 2.00 max | Maksimal 0,045 | Maksimal 1,00 | Maksimal 0,03 | 18.0-20.0 | 8.0-12.0 | Balans |
Mexanik xususiyatlar
| Mexanik xususiyatlari: | |||||
| Sinf | Qarshilik kuchi, MPa | Hosildorlik kuchi, MPa | Uzayish,% | Qattiqligicha,% | |
| Rokvell B (HRB) | Brinell (HB) | ||||
| 304 | 515 min | 205 min | 40 min | 92 | 201 |
| 304L | 485 min | 170 min | 40 min | 92 | 201 |
| 304H | 515 min | 205 min | 40 min | 92 | 201 |